omposites and adhesives. .

RA-9431


165 - 180

15,000 - 25,000
Low viscosity version of L-238 resin with a functionality of 2.2.

L-552


145 - 150

1000 - 1500
Low viscosity modified epoxy phenol novolac. Provides excellent
mechanical strength and chemical resistance. Used for coatings
and reinforced applications such as composites, wet lay-up,
filament winding and resin transfer moulding (RTM). Can obtain
Tg up to 135°C with Hardener K 552 on post-curing at 80
o
C.

RA-9281


165 - 180

3500 - 6500
Bisphenol-F epoxy with good flexibility, mechanical properties
and resistance to organic solvents. Used for coatings, tank
linings, secondary containment, flooring, civil engineering,
composites, and adhesives. Also utilized in filament winding,
pultrusion, and RTM applications.

RA-9282


165 - 175

3300 - 4100
Low viscosity Bisphenol-F epoxy resin.

XR-40


159 - 175

2000 - 5000
Low viscosity Bisphenol-F epoxy resin with tendency to
Crystallize. Used mainly in an 80:20 blend Bis-A/Bis-F with good
storage stability.

RA-9302


170 - 180

6500 - 8000
Bisphenol-F / Bisphenol-A blend produces a non-crystallizing,
low
viscosity
epoxy
for
flooring,
secondary
containment
and
civil
engineering applications. Also used for filament winding and
pultrusion applications.